| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Fatigue Strength (MPa) | |
|---|---|---|---|---|
| Aluminum 6061 | 60 | 2.68 | 193 | 117 |
| Aluminum 6063 | 73 | 2.7 | 214 | 68.9 |
| Aluminum 7050 | 147 | 2.83 | 490 | 160 |
| Aluminum 7075(Aerospace Grade) | 150 | 2.81 | 503 | 159 |
| Aluminum MIC-6 | 65 | 2.7 | 105 | N/A |
| Aluminum 5052 | 60 | 2.68 | 193 | 117 |
| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Fatigue Strength (MPa) | |
|---|---|---|---|---|
| Copper 101 | 65 - 90 | 8.89 - 8.94 | 69 - 365 | 76 - 90 |
| Copper C110 | 65 - 90 | 8.89 | 69 - 365 | 76 - 90 |
| Copper C172 | 80 - 85 | 8.25 | 515 - 585 | 275 |
| Copper C260 | 60 - 82 | 8.53 | 103 - 441 | 90 |
| Copper C360 | 63-130 | 8.49 | 124-310 | 138 |
| Brass CZ121 | 90 - 160 | 8.47 | 360 - 500 | 220 - 360 |
| Brass CZ131 | 70 - 140 | 8.5 | 340 - 480 | 200 - 350 |
| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Modulus of Elasticity (GPa) | Elongation at Break(%) | |
|---|---|---|---|---|---|
| Stainless Steel 17-7 | 388 | 7.8 | 1275 | 204 | 6 |
| Stainless Steel 301 | 217 | 8.03 | 205 | 212 | 40 |
| Stainless Steel 303 | 160 | 8.03 | 240 | 200 | 50 |
| Stainless Steel 316 | 187 | 8.03 | 205 | 193 | 40 |
| Stainless Steel 332 | 200 | 8.03 | 294 | 196 | 44 |
| Stainless Steel 416 | 360 | 7.8 | 962 | 200 | 9.5 |
| Stainless Steel 420 | 506 | 7.8 | 1040 | 200 | 11.5 |
| Stainless Steel 440C | 495 - 653 | 7.8 | 450 - 1900 | 204 - 215 | 2.0 - 14 |
| Hardness(Shore D) | Density (g/cm^3) | Modulus of Elasticity (GPa) | Tensile Strength(MPa) | Elongation at Break(%) | |
|---|---|---|---|---|---|
| HDPE | 50 - 76 | 0.92 - 0.99 | 0.565 - 1.5 | 11 - 43 | 3 - 80 |
| UHMW-PE | 54 - 120 | 0.8 - 1.8 | 0.3 - 1.1 | 11.6 - 40 | 3.5 - 800 |
| PVC | 80 | 1.16 - 1.65 | 1.82 - 7.03 | 3.45 - 73.1 | 2 - 330 |
| ABS/Nylon Blend | 64 | 1.04 - 1.21 | 0.9 - 5.3 | 27 - 100 | 3.1 - 230 |
| Acrylic | 60 | 0.7 - 1.3 | 0.95 - 3.79 | 25 - 85 | 1 - 85 |
| Nylon 66 | 76 - 88 | 1.02 - 2.7 | 0.6 - 25 | 10 - 98 | 1 - 300 |
| PTFE | 11 - 70 | 0.7 - 3.35 | 0.392 - 0.75 | 0.86 - 41.4 | 70 - 650 |
| PEEK | 62 - 94 | 1.26 - 1.72 | 2.14 - 24 | 11 - 125 | 1.7 - 100 |
| POM-H | 81 | 1.42 | 3.2 | 75 | 30 |
| POM-C | 79 | 1.41 | 2.8 | 67 | 40 |
| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Modulus of Elasticity (GPa) | Elongation at Break(%) | |
|---|---|---|---|---|---|
| Titanium(Grade 1) | 120 | 4.5 | 170 - 310 | 103 | 24 |
| Titanium(Grade 2) | 200 | 4.51 | 276 - 448 | 103 | 20 |
| Titanium(Grade 4) | 265 | 4.51 | 480 - 655 | 105 | 15 |
| Ti-6Al-4V(Grade 5) | 379 | 4.43 | 1100 | 114 | 10 |
| Bronze | 11.6 - 420 | 5.6 - 14 | 69 - 800 | 72.4 - 138 | 0 - 70 |
| Zinc Alloy (Zamak 5) | 91 | 6.7 | 208 | 70 - 100 | 7 |
| Steel Alloy AISI 4340 | 388 | 7.85 | 972 | 200 | 12.1 |
| Nickel Alloy | 175 - 240 | 8.44 | 414 - 758 | 207 | 16 |