Copper is characterized by its resistance to corrosion, excellent electrical conductivity, and significant malleability. The metal’s distinctive reddish-orange color is easily identifiable, and it maintains its visual appeal even as it naturally oxidizes, forming a greenish-blue layer called patina.
Copper C101
Copper C110
Copper C172
Copper C260
Copper C360
CNC machining produces parts with excellent mechanical properties, accuracy and repeatability from metal and plastic. 3-axis & 5-axis CNC milling available.
Jingbang provides extensive copper CNC machining services, capable of fabricating intricate components from a variety of copper materials. Known for their resistance to corrosion, copper parts are adaptable for uses that demand electrical conductivity and visual appeal. Utilizing a wide range of CNC mills and turning centers, we can manufacture any required part
Jingbang has been engaged in CNC machining industry for 13 years, more than 50 kinds of metal and plastic materials have a wealth of machining experience, the following materials are commonly used in our production of copper materials
It has a very high percentage of Copper in it – 99.9%.
| Cu % | Bal % |
|---|---|
| Others | ≤0.10 |
| Tensile strength (MPa) | Conditional yield strength (MPa) | Elongation (%) | Hardness |
|---|---|---|---|
| 200 | 60 – 240 | 5 – 50 | HB60 – 90 |
It has a very high percentage of Copper in it – 99.9%.
| Cu % | O % |
|---|---|
| Others | ≤0.05 |
| Tensile strength (MPa) | Conditional yield strength (MPa) | Elongation (%) | Hardness |
|---|---|---|---|
| ≥290 | ≥250 | 3 – 16 | HR54 – 62 |
| Cu % | Be % | Co+Ni % | Co+Ni+Fe % | Pb % | Other |
|---|---|---|---|---|---|
| ≥97 | 1.8 – 2.0 | ≥0.20 | ≤0.60 | ≤0.10 | ≤0.50 |
| Tensile strength (MPa) | Conditional yield strength (MPa) | Elongation (%) | Hardness, Rockwell B |
|---|---|---|---|
| 415 – 585 | 415 – 605 | 10 – 36 | 45 – 85 |
| Cu % | Zn % | Fe % | Pb % | Other |
|---|---|---|---|---|
| 68.5 – 71.5 | 28.5 – 31.5 | ≤0.05 | ≤0.07 | ≤0.15 |
| Tensile strength (MPa) | Conditional yield strength (MPa) | Elongation (%) | Hardness, Rockwell F |
|---|---|---|---|
| 300 | 68 | ≥20 | 54 |
| Cu % | Zn % | Fe % | Pb % |
|---|---|---|---|
| 60 – 63 | 33.3 – 36.9 | ≤0.35 | 3.1 – 3.7 |
| Tensile Strength(Mpa) | Elongation (%) | Tensile Modulus(Gpa) | Hardness, Rockwell B |
|---|---|---|---|
| 386 | 20 | 96.5 | 62 |
If your project requires other materials, please Contact us, material-related data and suitability assessment for your project will be sent to you promptly.
Copper’s excellent conductivity makes it ideal for high-power electronics. With the rise of electric vehicles, demand for copper wiring is growing. From TVs to home appliances, its ductility ensures easy use in tight spaces.
Learn more about Materials in Jingbang’s Resource Hub
Learn all about our full range of rapid prototyping and CNC machining services—contact Jingbang today. With a team of experienced engineers, we are ready to provide expert guidance and support at every step. Reach out for a free quote within 24 hours and enjoy a DFM analysis within 48 hours.
| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Fatigue Strength (MPa) | |
|---|---|---|---|---|
| Aluminum 6061 | 60 | 2.68 | 193 | 117 |
| Aluminum 6063 | 73 | 2.7 | 214 | 68.9 |
| Aluminum 7050 | 147 | 2.83 | 490 | 160 |
| Aluminum 7075(Aerospace Grade) | 150 | 2.81 | 503 | 159 |
| Aluminum MIC-6 | 65 | 2.7 | 105 | N/A |
| Aluminum 5052 | 60 | 2.68 | 193 | 117 |
| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Fatigue Strength (MPa) | |
|---|---|---|---|---|
| Copper 101 | 65 - 90 | 8.89 - 8.94 | 69 - 365 | 76 - 90 |
| Copper C110 | 65 - 90 | 8.89 | 69 - 365 | 76 - 90 |
| Copper C172 | 80 - 85 | 8.25 | 515 - 585 | 275 |
| Copper C260 | 60 - 82 | 8.53 | 103 - 441 | 90 |
| Copper C360 | 63-130 | 8.49 | 124-310 | 138 |
| Brass CZ121 | 90 - 160 | 8.47 | 360 - 500 | 220 - 360 |
| Brass CZ131 | 70 - 140 | 8.5 | 340 - 480 | 200 - 350 |
| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Modulus of Elasticity (GPa) | Elongation at Break(%) | |
|---|---|---|---|---|---|
| Stainless Steel 17-7 | 388 | 7.8 | 1275 | 204 | 6 |
| Stainless Steel 301 | 217 | 8.03 | 205 | 212 | 40 |
| Stainless Steel 303 | 160 | 8.03 | 240 | 200 | 50 |
| Stainless Steel 316 | 187 | 8.03 | 205 | 193 | 40 |
| Stainless Steel 332 | 200 | 8.03 | 294 | 196 | 44 |
| Stainless Steel 416 | 360 | 7.8 | 962 | 200 | 9.5 |
| Stainless Steel 420 | 506 | 7.8 | 1040 | 200 | 11.5 |
| Stainless Steel 440C | 495 - 653 | 7.8 | 450 - 1900 | 204 - 215 | 2.0 - 14 |
| Hardness(Shore D) | Density (g/cm^3) | Modulus of Elasticity (GPa) | Tensile Strength(MPa) | Elongation at Break(%) | |
|---|---|---|---|---|---|
| HDPE | 50 - 76 | 0.92 - 0.99 | 0.565 - 1.5 | 11 - 43 | 3 - 80 |
| UHMW-PE | 54 - 120 | 0.8 - 1.8 | 0.3 - 1.1 | 11.6 - 40 | 3.5 - 800 |
| PVC | 80 | 1.16 - 1.65 | 1.82 - 7.03 | 3.45 - 73.1 | 2 - 330 |
| ABS/Nylon Blend | 64 | 1.04 - 1.21 | 0.9 - 5.3 | 27 - 100 | 3.1 - 230 |
| Acrylic | 60 | 0.7 - 1.3 | 0.95 - 3.79 | 25 - 85 | 1 - 85 |
| Nylon 66 | 76 - 88 | 1.02 - 2.7 | 0.6 - 25 | 10 - 98 | 1 - 300 |
| PTFE | 11 - 70 | 0.7 - 3.35 | 0.392 - 0.75 | 0.86 - 41.4 | 70 - 650 |
| PEEK | 62 - 94 | 1.26 - 1.72 | 2.14 - 24 | 11 - 125 | 1.7 - 100 |
| POM-H | 81 | 1.42 | 3.2 | 75 | 30 |
| POM-C | 79 | 1.41 | 2.8 | 67 | 40 |
| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Modulus of Elasticity (GPa) | Elongation at Break(%) | |
|---|---|---|---|---|---|
| Titanium(Grade 1) | 120 | 4.5 | 170 - 310 | 103 | 24 |
| Titanium(Grade 2) | 200 | 4.51 | 276 - 448 | 103 | 20 |
| Titanium(Grade 4) | 265 | 4.51 | 480 - 655 | 105 | 15 |
| Ti-6Al-4V(Grade 5) | 379 | 4.43 | 1100 | 114 | 10 |
| Bronze | 11.6 - 420 | 5.6 - 14 | 69 - 800 | 72.4 - 138 | 0 - 70 |
| Zinc Alloy (Zamak 5) | 91 | 6.7 | 208 | 70 - 100 | 7 |
| Steel Alloy AISI 4340 | 388 | 7.85 | 972 | 200 | 12.1 |
| Nickel Alloy | 175 - 240 | 8.44 | 414 - 758 | 207 | 16 |