Jingbang offers various CNC machining materials, including metals and plastics.
We can produce high-quality, competitively priced metal and plastic parts within your deadline. Whether you need prototypes or custom parts, we have what you need for your project.
The factory strictly selects materials to reduce cost and increase efficiency, and professional testing to meet international standards.
Jingbang offers over 30 standard Materials. A team of professional engineers can help you select the right materials for your project.
We adhere to strict testing procedures and will provide you with the required certifications, as well as accept third party testing.
A wide range of metals can be used for CNC machining, and the choice should depend on mechanical properties, thickness and desired shape. Check out the most common metals and their unique properties and benefits.
Materials | Description | Common Applications | Price | |
|---|---|---|---|---|
| Steel |  | Steel is used in CNC machining for structural components and machinery parts. | Good matte surface finish that makes it suitable for exposed parts. Gears, shafts, pins, bolts and nuts, pump and valve components | $$$ |
| Stainless Steel |  | Designed for machining, non-magnetic, corrosion-resistant and durable | Electronic hardware, automotive, aerospace, medical instruments, and many applications requiring corrosion resistance | $$$ |
| Aluminum |  | Lightweight and versatile, aluminum offers excellent machinability and corrosion resistance | Electronic hardware, aircraft components, automotive parts, structural applications | $ |
| Titanium |  | High strength, light weight, good bio-compatibility, strong and corrosion-resistant | Medical implants, aircraft and aerospace parts | $$$$$ |
| Carbon Fiber |  | Strong, lightweight, and stiff material that is made from thin, strong crystalline filaments of carbon | Aircraft and spacecraft parts, racing car bodies, golf club shafts, bicycle frames, fishing rods, automobile springs, sailboat masts | $$$ |
| Copper |  | High corrosion resistance, conductivity, and finish. Non-magnetic and has a very low permeability. | Magnetic housings, Electrical contacts, Bushings, Bearings, Pump components | $$$ |
| Plastic |  | High impact strength and durability, resistance to frictional wear, weathering, flame, heat, chemical, and radiation | Insulators, Bearings, Spacers, Valve components, low moisture absorption rate, making it suitable for use in wet environments | $$ |
Didn’t find the material you were looking for? Contact us and our team of experts will be happy to review the project and introduce you to the needed materials. See Resource Hub for more information on materials.
Steel’s wide choice of alloys and versatility make it useful in a variety of industrial applications
Steel’s wide choice of alloys and versatility make it useful in a variety of industrial applications
Learn more about Materials in Jingbang’s Resource Hub
Learn all about our full range of rapid prototyping and CNC machining services—contact Jingbang today. With a team of experienced engineers, we are ready to provide expert guidance and support at every step. Reach out for a free quote within 24 hours and enjoy a DFM analysis within 48 hours.
| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Fatigue Strength (MPa) | |
|---|---|---|---|---|
| Aluminum 6061 | 60 | 2.68 | 193 | 117 |
| Aluminum 6063 | 73 | 2.7 | 214 | 68.9 |
| Aluminum 7050 | 147 | 2.83 | 490 | 160 |
| Aluminum 7075(Aerospace Grade) | 150 | 2.81 | 503 | 159 |
| Aluminum MIC-6 | 65 | 2.7 | 105 | N/A |
| Aluminum 5052 | 60 | 2.68 | 193 | 117 |
| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Fatigue Strength (MPa) | |
|---|---|---|---|---|
| Copper 101 | 65 - 90 | 8.89 - 8.94 | 69 - 365 | 76 - 90 |
| Copper C110 | 65 - 90 | 8.89 | 69 - 365 | 76 - 90 |
| Copper C172 | 80 - 85 | 8.25 | 515 - 585 | 275 |
| Copper C260 | 60 - 82 | 8.53 | 103 - 441 | 90 |
| Copper C360 | 63-130 | 8.49 | 124-310 | 138 |
| Brass CZ121 | 90 - 160 | 8.47 | 360 - 500 | 220 - 360 |
| Brass CZ131 | 70 - 140 | 8.5 | 340 - 480 | 200 - 350 |
| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Modulus of Elasticity (GPa) | Elongation at Break(%) | |
|---|---|---|---|---|---|
| Stainless Steel 17-7 | 388 | 7.8 | 1275 | 204 | 6 |
| Stainless Steel 301 | 217 | 8.03 | 205 | 212 | 40 |
| Stainless Steel 303 | 160 | 8.03 | 240 | 200 | 50 |
| Stainless Steel 316 | 187 | 8.03 | 205 | 193 | 40 |
| Stainless Steel 332 | 200 | 8.03 | 294 | 196 | 44 |
| Stainless Steel 416 | 360 | 7.8 | 962 | 200 | 9.5 |
| Stainless Steel 420 | 506 | 7.8 | 1040 | 200 | 11.5 |
| Stainless Steel 440C | 495 - 653 | 7.8 | 450 - 1900 | 204 - 215 | 2.0 - 14 |
| Hardness(Shore D) | Density (g/cm^3) | Modulus of Elasticity (GPa) | Tensile Strength(MPa) | Elongation at Break(%) | |
|---|---|---|---|---|---|
| HDPE | 50 - 76 | 0.92 - 0.99 | 0.565 - 1.5 | 11 - 43 | 3 - 80 |
| UHMW-PE | 54 - 120 | 0.8 - 1.8 | 0.3 - 1.1 | 11.6 - 40 | 3.5 - 800 |
| PVC | 80 | 1.16 - 1.65 | 1.82 - 7.03 | 3.45 - 73.1 | 2 - 330 |
| ABS/Nylon Blend | 64 | 1.04 - 1.21 | 0.9 - 5.3 | 27 - 100 | 3.1 - 230 |
| Acrylic | 60 | 0.7 - 1.3 | 0.95 - 3.79 | 25 - 85 | 1 - 85 |
| Nylon 66 | 76 - 88 | 1.02 - 2.7 | 0.6 - 25 | 10 - 98 | 1 - 300 |
| PTFE | 11 - 70 | 0.7 - 3.35 | 0.392 - 0.75 | 0.86 - 41.4 | 70 - 650 |
| PEEK | 62 - 94 | 1.26 - 1.72 | 2.14 - 24 | 11 - 125 | 1.7 - 100 |
| POM-H | 81 | 1.42 | 3.2 | 75 | 30 |
| POM-C | 79 | 1.41 | 2.8 | 67 | 40 |
| Hardness (Brinell) | Density (g/cm^3) | Tensile Strength(MPa) | Modulus of Elasticity (GPa) | Elongation at Break(%) | |
|---|---|---|---|---|---|
| Titanium(Grade 1) | 120 | 4.5 | 170 - 310 | 103 | 24 |
| Titanium(Grade 2) | 200 | 4.51 | 276 - 448 | 103 | 20 |
| Titanium(Grade 4) | 265 | 4.51 | 480 - 655 | 105 | 15 |
| Ti-6Al-4V(Grade 5) | 379 | 4.43 | 1100 | 114 | 10 |
| Bronze | 11.6 - 420 | 5.6 - 14 | 69 - 800 | 72.4 - 138 | 0 - 70 |
| Zinc Alloy (Zamak 5) | 91 | 6.7 | 208 | 70 - 100 | 7 |
| Steel Alloy AISI 4340 | 388 | 7.85 | 972 | 200 | 12.1 |
| Nickel Alloy | 175 - 240 | 8.44 | 414 - 758 | 207 | 16 |